Skip navigation
Use este identificador para citar ou linkar para este item: http://repositorio.unb.br/handle/10482/12569
Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
ARTIGO_CementContentInfluence.pdf1,84 MBAdobe PDFVisualizar/Abrir
Registro completo de metadados
Campo DCValorIdioma
dc.contributor.authorPessoa, Patricia Oliveira Americo-
dc.contributor.authorNepomuceno, Antônio Alberto-
dc.date.accessioned2013-03-22T21:09:28Z-
dc.date.available2013-03-22T21:09:28Z-
dc.date.issued2003-
dc.identifier.citationAMÉRICO, P. O.; NEPOMUCENO, A. A. Influencia del contenido en cemento en la corrosión de la armadura en morteros carbonatados. Materiales de Construcción, Madrid, v. 53, n. 271-273, 2003. Disponível em: <http://materconstrucc.revistas.csic.es/index.php/materconstrucc/article/view/296>. Acesso em: 15 mar. 2013. _______________________________________________________________________________________________________en
dc.identifier.citationAMÉRICO, P. O.; NEPOMUCENO, A. A. Cement content influence in rebar corrosion in carbonated mortars. Materiales de Construcción, Madrid, v. 53, n. 271-273, 2003. Disponível em: <http://materconstrucc.revistas.csic.es/index.php/materconstrucc/article/view/296>. Acesso em: 15 mar. 2013.en
dc.identifier.urihttp://repositorio.unb.br/handle/10482/12569-
dc.description.abstractLos productos de hidratación del cemento protegen las armaduras embebidas en el hormigón debido a la gran cantidad de Ca(OH)2, NaOH y KOH disueltos en la fase acuosa del hormigón que proporcionan un pH mayor que 12,5. Sin embargo, las estructuras de hormigón armado están expuestas a los gases contaminantes como el CO2, que al penetrar en el hormigón reacciona con los compuestos alcalinos, se reduce el pH de la fase acuosa y provocan la despasivación de la armadura. Posteriormente, si hay disponibilidad de humedad y oxígeno empieza la corrosión. El objetivo del presente trabajo es analizar la influencia del contenido en cemento, en la corrosión de armaduras en medios carbonatados empleando la técnica de Resistencia de polarización para la determinación de la intensidad de corrosión. Se presentan resultados de intensidad de corrosión de armaduras embebidas en probetas prismáticas de mortero fabricadas con tres dosificaciones de cemento con igual relación agua/cemento. También se emplearon probetas cilíndricas para medidas de absorción capilar antes y después de la carbonatación. Las características de porosidad fueron evaluadas por porosimetría de intrusión de mercurio antes y después de la carbonatación. Los resultados muestran que cuando el contenido en cemento disminuye el período de iniciación es menor y la intensidad de corrosión en la propagación mayor Sin embargo, también hay una alteración de la microestructura con los cambios en la cantidad de cemento, lo que impide afirmar que la reserva alcalina aisladamente sea la responsable de estos resultados. ________________________________________________________________________________________________________________ ABSTRACTen
dc.description.abstractThe cement hydration products protect the concrete rebars of the reinforced concrete due to the production of Ca(OH)2, NaOH, and KOH that, upon dissolving in the concrete s aqueous phase, generate a pH above 12.5. However, reinforced concrete structures are exposed to pollutant gases, such as, CO2 which upon penetrating the concrete, reacts with the alkaline components, consequently reducing the pH of the aqueous phase causing the loss of passivity by the rebar and as a consequence its corrosion when there is the presence of humidity and oxygen. The objective of the current paper is the analysis of the alkaline reserve influence, measured by the cement content, in the corrosion of rebars employing the polarization resistance technique for determining the corrosion intensity. Results for corrosion intensity of rebars embedded in prismatic mortar test specimens are produced with three cement content levels, with equal water/cement ratio. Cylindrical test specimens were also used for verification of the capillary absorption and the porosity by means of mercury porosymetry The results show that the initiation period is shorter and the corrosion intensity of the rebars is higher when the cement content is lower However, there is also an alteration in the microstructure upon altering the cement content, and far this reason one cannot conclude that the alkaline reserve alone is responsible for these results.en
dc.language.isoInglêsen
dc.language.isoEspanholen
dc.publisherInstituto Técnico de la Construcción y del Cementoen
dc.rightsAcesso Abertoen
dc.titleInfluencia del contenido en cemento en la corrosión de la armadura en morteros carbonatadosen
dc.title.alternativeCement content influence in rebar corrosion in carbonated mortarsen
dc.typeArtigoen
dc.subject.keywordMateriais - deterioraçãoen
dc.subject.keywordCorrosão e anticorrosivosen
dc.subject.keywordCarbonataçãoen
dc.subject.keywordCimentoen
dc.rights.licenseMateriales de Construcción - Licenciada sob uma Licença Creative Commons (Reconocimiento-NoComercial 3.0 España (CC BY-NC 3.0 ES)). Fonte: http://materconstrucc.revistas.csic.es/index.php/materconstrucc/article/view/296. Acesso em: 15 mar. 2013.en
Aparece nas coleções:Artigos publicados em periódicos e afins

Mostrar registro simples do item Visualizar estatísticas



Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.