Título: Production and properties of a new wood laminated veneer/high-density polyethylene composite board
Autor(es): Lustosa, Emanuela Camargo de Barros
Del Menezzi, Cláudio Henrique Soares
Melo, Rafael Rodolfo de
Assunto: Lâminas de madeira
Sacolas plásticas
Reciclagem
Data de publicação: Set-2015
Editora: ABM, ABC, ABPol
Referência: LUSTOSA, Emanuela Camargo de Barros; DEL MENEZZI, Cláudio Henrique Soares; MELO, Rafael Rodolfo de. Production and properties of a new wood laminated veneer/high-density polyethylene composite board. Materials Research, São Carlos, v. 18, n. 5, p. 994-999, set./out. 2015. Disponível em: <http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392015000500994&lng=en&nrm=iso>. Acesso em: 3 abr. 2018. doi: http://dx.doi.org/10.1590/1516-1439.010615.
Abstract: The paper aimed at evaluating the feasibility and the properties of a new product which combines wood veneer and high-density polyethylene (HDPE) from post-consuming plastic bags. Three HDPE amounts were evaluated: 150g/m2, 250 g/m2 e 350 g/m2. The boards were manufactured using a single-opening hot-press under such conditions: 140ºC, for 20 minutes and pressure of 1 N/mm2. It was found that the production of this kind of composite board is technically possible and relatively simple and they did not present any veneer delamination. The properties of the composite boards were quite similar or even higher to those found in LVL made using thermosetting resin. The higher the HDPE amount the higher the density of the composite board, which imparted significantly in mechanical properties. However, when the composite boards were evaluated under same density the effect of the HDPE amount affected only Janka hardness.
Licença: Materials Research - This is an Open Access article distributed under the terms of the Creative Commons Attribution License, which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited (CC BY 4.0). Fonte: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392015000500994&lng=en&nrm=iso. Acesso em: 3 abr. 2018.
DOI: http://dx.doi.org/10.1590/1516-1439.010615
Aparece nas coleções:Artigos publicados em periódicos e afins

Mostrar registro completo do item Visualizar estatísticas



Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.