Título : Effect of cerium loading on structure and morphology of modified Ce-USY zeolites
Autor : Garcia, Fillipe Augusto da Costa
Araújo, Daniel Ribeiro
Silva, Júnia Chaves Marinho e
Macedo, Julio Lemos de
Ghesti, Grace Ferreira
Dias, Sílvia Cláudia Loureiro
Dias, José Alves
Rocha Filho, Geraldo N.
Assunto:: Zeólitas
Óxido de cério
Troca iônica
Espectroscopia de Raman
Ressonância magnética nuclear
Fecha de publicación : oct-2011
Editorial : Sociedade Brasileira de Química
Citación : GARCIA, Fillipe A. C. et al. Effect of cerium loading on structure and morphology of modified Ce-USY zeolites. Journal of the Brazilian Chemical Society, São Paulo, v. 22, n. 10, p. 1894-1902, out. 2011. DOI: http://dx.doi.org/10.1590/S0103-50532011001000010. Disponível em: http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0103-50532011001000010&lng=en&nrm=iso. Acesso em: 12 jan. 2021.
Resumen : Este trabalho descreve detalhadamente o efeito da quantidade de cério na estrutura e morfologia da zeólita NH4USY. Ce-USY (2-25% m/m de CeO2) foi obtido por impregnação úmida de CeCl3 seguida de calcinação a 550ºC por 8 h. Em quantidades baixas (2-10%), foi observado que as espécies de cério encontram-se nas posições de troca iônica na rede, enquanto em maiores teores (15-25%) pequenos agregados formaram-se na superfície da HUSY. Difratometria de raios X (XRD) mostrou apenas reflexões relacionadas à HUSY, confirmando a alta dispersão das espécies de cério, porém as análises por espectroscopia Raman com transformada de Fourier (FT-Raman) detectaram CeOx para os materiais acima de 10%. A reação do CeCl3 com NH4USY produziu NH4Cl, o qual se decompõe em HCl, ocasionando a desaluminização da rede. Os materiais apresentaram um aumento da razão Lewis/Brønsted com o aumento da quantidade de cério, devido a interação do excesso de cério com os grupos OH da USY e consequente formação de espécies CeOx.
Abstract: This work describes comprehensibly the effect of cerium loading on the structure and morphology of NH4USY zeolite. The Ce-USY (2-25 wt.% of CeO2) was obtained by wet impregnation of CeCl3 followed by calcination at 550ºC for 8 h. At low loadings (2-10%), cerium species are mainly located at ion exchange positions in the framework, whereas at higher loadings (15-25%), small aggregates were formed on the HUSY surface. X-ray diffractograms (XRD) exhibited only the reflections related to HUSY, demonstrating the high dispersion of cerium species, but Fourier transform Raman spectroscopy (FT-Raman) detected CeOx for the materials above 10%. Reaction of CeCl3 with NH4USY produced NH4Cl, which decomposed to form HCl, leading to framework dealumination. The materials showed an increased Lewis/Brønsted ratio with increasing cerium loadings due to the interaction between the excess cerium and the OH groups of USY, and the consequent formation of CeOx species.
metadata.dc.description.unidade: Instituto de Química (IQ)
Licença:: Journal of the Brazilian Chemical Society - All the contents of this journal, except where otherwise noted, is licensed under a Creative Commons Attribution License (CC BY NC 4.0). Fonte: https://www.scielo.br/scielo.php?script=sci_arttext&pid=S0103-50532011001000010&lng=en&nrm=iso&tlng=en. Acesso em: 12 jan. 2021.
DOI: https://dx.doi.org/10.1590/S0103-50532011001000010
Aparece en las colecciones: Artigos publicados em periódicos e afins

Mostrar el registro Dublin Core completo del ítem " class="statisticsLink btn btn-primary" href="/jspui/handle/10482/28086/statistics">



Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.