Título: Evaluation of mechanical properties and microstructure of high-performance mortars with superabsorbent polymers and metakaolin by means of X-ray computed microtomography
Autor(es): Silva, Arthur Aviz Palma e
Capuzzo, Valdirene Maria Silva C.
Silva, Eugênia Fonseca
Pereira, André Maues Brabo
Silva, Douglas Aviz Palma e
Afiliação do autor: University of Brasília, Graduate Program in Structures and Civil Construction
University of Brasília, Graduate Program in Structures and Civil Construction
University of Brasília, Graduate Program in Structures and Civil Construction
Federal Fluminense University
State University of Pará
Assunto: Polímero superabsorvente
Concreto de alto desempenho
Microtomografia de raios X
Data de publicação: Fev-2022
Editora: lsevier Ltd.
Referência: SILVA, Arthur Aviz Palma e et al. Evaluation of mechanical properties and microstructure of high-performance mortars with superabsorbent polymers and metakaolin by means of X-ray computed microtomography. Journal of Building Engineering, v. 51, 104219, 2022. DOI: https://doi.org/10.1016/j.jobe.2022.104219
Abstract: Superabsorbent polymers (SAP) may provide internal curing in cementitious materials, conse- quently, they reduce autogenous shrinkage caused by low water/cement ratios and autodesse- cation of pores. This paper aimed to analyze the effect of Superabsorbent polymers in high- strength mortars, using metakaolin as supplementary cementitious material (SCM). A X-ray microtomography test was carried out on two mixtures of mortars, a reference mix (MKREF) and a mix containing 0.30% superabsorbent polymer (MKSAP30), and the acquired images enabled the evaluation of mortar phases, anhydrate cement and void content. Also, a compressive strength test was carried out at 3 ages for both mixtures. The superabsorbent polymer was added still dry in the mixture, and no extra water was used for SAP absorption, hence, all the mixtures had the same total water/cement ratios. The results point to an increase in mechanical properties on mortars modified with SAP of 51% at the age of 28 days. Also, a higher porosity was observed in MKSAP30 samples, however, the pores were of small diameters, showing that SAP may provide refinement in pores of the cement matrix. In addition, a higher pore connectivity was detected, and an increase in the number of pores accounted using microtomographic images and the software called Fiji/ImageJ software for MKSAP30. The SAP modified mortar also showed more pores tortuosity. Finally, a lower percentage of anhydrate cement remaining in the mixture with SAP was shown, pointing to an optimization of the hydration degree, corroborating to the improvement of mechanical properties.
Unidade Acadêmica: Faculdade de Tecnologia (FT)
Departamento de Engenharia Civil e Ambiental (FT ENC)
Programa de pós-graduação: Programa de Pós-Graduação em Estruturas e Construção Civil
DOI: https://doi.org/10.1016/j.jobe.2022.104219
Versão da editora: https://www.sciencedirect.com/science/article/pii/S2352710222002327?via%3Dihub
Aparece nas coleções:Artigos publicados em periódicos e afins

Mostrar registro completo do item Visualizar estatísticas



Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.